NEWS
- Drug transport across nylon 610 films: influence of synthesi
- Spherulites in nylon 610 and nylon 66
- Special material for fishing line production - nylon PA612 drawing grade product
- Extrusion grade nylon PA12 raw material for tennis racket sheath
- High toughness, high impact strength and high abrasion resistance resin PA612 is used to make brushe
- Nylon 612 has good abrasion resistance and is used to make hoses
- PA610 is used to make high impact strength and high toughness bushings
PRODUCTS>>
Nylon PA610 Resin
Polyamide 610 - Nylon 610 - PA 610
PA610 Molecular Formula:(C16H30N2O2)n
PA610 Structural Formula:
PA610 Features:Compare with the the Nylon 6 and the Nylon 66, the nylon 610 is more softer, has low water absorption, better resistance to low temperature and dimensional stability. It has good oil resistance, chemical resistance and electric specification, belongs to the selfextingushing material.
PA610 Application:
It is mainly used as the toothbrush's bristlelike monofilament, filaments for brushes,monofilament, battery case,cable covering, zip fasteners, slide way,electrical insulators and precision parts,etc.
PA610 Index:
| Test Items | UNIT | Standard Parameter Value | ||
| Ⅰ | Ⅱ | Ⅲ | ||
| Viscosity Number | g/ml | 105±15 | 135±15 | 180±20 |
| Loss on Drying | ‰ | ≤1.0 | ||
| Granularity | N/g | 30-50 | ||
| Melting Point | ℃ | 208-222 | ||
| Relative Density | G/cm3 | 1.08-1.12 | ||
| Tensile Strength | MPa | ≥55 | ||
| Elongation At Break | % | ≥150 | ||
| Flexural Strength | MPa | ≥60 | ||
| Test Items | UNIT | PA610 Resin | |||
| A6G6301 | A6G7301 | A6MG9301 | A6G9301-G | ||
| Tensile Strength | MPa | 114 | 146 | 153 | 161 |
| Elongation At Break | % | 502 | 317 | 426 | 295 |
| Charpy Notch Impact | KJ/m2 | 27 | 18 | 16 | 19 |
| Charpy Non-Notch Impact | KJ/m2 | 93 | 96 | 88 | 82 |
| Flexural Strength | MPa | 156 | 202 | 228 | 230 |
| Flexural Module | MPa | 5100 | 7600 | 9325 | 9675 |
| Ash Content | % | 30 | 35 | 45 | 45 |
* Note:Tell me about your parameters, Lyuechem company will give you a more satisfactory answer.